Phase formation in mixed TiO2-ZrO2 oxides prepared by sol-gel method
2011
Pure titania, zirconia, and mixed oxides (3—37 mol.% of ZrO2) are prepared using the sol-gel method and calcined at different temperatures. The calcined samples are characterized by Raman spectroscopy, X-ray powder diffraction, scanning electron microscopy, transmission electron microscopy, and nitrogen adsorption porosimetry. Measurements reveal a thermal stability of the titania anatase phase that slightly increases in the presence of 3—13 mol.% of zirconia. Practically, the titania anatase-rutile phase transformation is hindered during the temperature increase above 700 C. The mixed oxide with 37 mol.% of ZrO2 treated at 550 C shows a new single amorphous phase with a surface area of the…
Mechanical treatment of TiO2 and ZrO2 oxide mixtures
2010
The mixed ZrO2–TiO2 system (5–50 wt% of ZrO2) has been studied to investigate the influence of the mechanical treatment on its physicochemical properties depending on the composition, time of milling (5, 10 and 20 min, r.p.m. 82) and temperature (400, 550 and 700 C). Samples were characterized by Raman spectroscopy, X-ray powder diffraction, Scanning Electron Microscopy coupled with Energy Dispersion X-ray analyzer, High Resolution-Transmission Electron Microscopy and nitrogen adsorption porosimetry. Results show that srilankite (TiZrO4) phase has been produced. No influence of the milling time and temperature on the phase composition is observed. The presence of zirconia increases the ther…